Density |
0.5-0.7g/cc |
Dielectric Loss Factor |
2.10 320.103 |
Tensile Strength |
181kg/cm2 |
Thermal Conductivity |
25mm Section 0.0616 : w/m.k |
Elongation |
15% |
K-Value |
25 MM Section 1.8 w/m2k |
Impact Strength |
32j/m |
Coefficient of Dilation at 20°C |
0.6 - 0.7 |
Shore Hardness |
Min 60 |
Dielectric Strength |
10kv |
Vicat Softening Point |
72°C |
Water Absorption percentage |
0.7 |
Elastic Modulus |
1000-1400 N/mm2 |
Fire Retardancy |
Self Extinguishable |
Flexural Strength |
374kg/cm2 |
Mechanical Strength |
Conforms to CI.No.5.4 of IS:5133(Pt.2)-1969 |
Surface Resistant |
5.1013 |
Stability at High Temperature |
CI. No. 5.6 of IS : 5133(Pt.2) - 1969 |
Dielectric Puncture Strength |
60kv/cm |
Resistance to abnormal heat and Fire |
CI. No. 9.15 of IS : 8828 - 1996 |
Flammability |
France |
NF P92-501 |
M1 |
Great Britain |
BS 476 Part 7 |
Class 1 |
United States |
UL 94 |
V-0 |
|
Relative Permitivity Range |
1.9 - 2.0 |
|
|